Hardness
(Guaranteed values) |
HBW
280-330 (Approx. 30-35 HRC) |
|
Impact properties
(Guaranteed values) |
|
Testing temperature °C
20-400°C |
Impact energy, Charpy-V,
longitudinal direction;
min. ft. lbs. < 74-133 |
|
|
Tensile Properties
(Calculated values) |
Tensile strength approx. 130 -
142,000 PSI |
|
Milling
(Calculated values) |
At cutting speed of 300 m/mm,
feed 0.15 mm, 10 min. effective cutting time using a Sandvik Coromil 200
and inserts GC 1025, we guarantee max 0.3 mm edge wear. |
|
Ultrasonic insp.
(Guaranteed values) |
Discontinuities giving echoes
at least equivalent in amplitude to flat bottom hole 1.5 mm shall be
reported according to SSAB Standard V6. |
|
Etching properties
(Guaranteed values) |
TOOLOX 33 fulfills the demands
according to NADCA 207-97. |
|
Dimensions
(Preliminary) |
TOOLOX 33 is supplied in plate
thickness 3/4” - 5 1/8”. |
|
Delivery condition |
Quenched and tempered at min.
590°C |
|
Heat treatment |
TOOLOX 33 is not intended for
further heat treatment If TOOLOX 33 is subjected to any heat treatment
above 590°C, after delivery from SSAB Oxelösund AB, no guarantees
concerning the properties of the matrial will be given. |
|
Testing |
Testing in accordance with EN
10 137-1, 10 137-2 and EN ISO 6506-1. Hardness measured on a milled
surface, 0,5-2 mm below surface. |
|
Tolerances |
According to EN 10 029
|
|
Surface finish |
According to EN 10 163-2
|