Processing Guidelines:

  • Machining
    Use of PX5 assures the longest cutting tool life of any 30 HRc, P20-type material and an overall 20-30% improvement in machining efficiency.

    Note: Positive, effective cutting rake angles are recommended, as are inserts with concave faces and chip breaking edges. TiAlN coatings work well.


  • Machinability
    A recent machining test was performed on PX5 material at a mold base manufacturer. Listed below are the tool settings for P20 and the results achieved with PX5.

Tool No. 1
1.250 Diameter DIJET Ballnose Endmill

  P20 PX5
RPM 986 1600
Feed (in/min) 11.83 27.60
Depth .120 .120

Program time was reduced from 38 minutes to 15.2 minutes

Tool No. 2
1.000 Diameter Waukesha Ballnose Endmill
 

  P20 PX5
RPM 1600 3000
Feed (in/min) 16.6 33.0
Depth (Contour) .160-.180 .160-.180

Program time was reduced from 5.7 minutes to 2.85minutes

Tool No. 3
.750 Sandvik Ballnose Endmill

  P20 PX5
RPM 2660 3000
Feed (in/min) 18.2 36.0
Depth (Step Over) .160 .160

Program time was reduced from 4.91 minutes to 2.5 minutes

Tool No. 4
(Finish cutter) 1.000 Diameter Iscar Ballnose Endmill

  P20 PX5
RPM 2419 3000
Feed (in/min) 19.35 40.00
Depth .060 .060

Program time was reduced from 10 minutes to 4.85 minutes


Note: There was no noticeable wear in any of the cutting tools using PX5.


  • Manufacturing Process
    A 40" x 41" x 87" block of PX5 was forged and heat treated. The piece was cut through 61" into the 87" length. The following hardness readings were taken across the face of the test piece.



 

  • Inspection Result
    Sectional Hardness Rockwell C Scale:

  • EDM
    The recast layer from EDM for PX5 is soft, approximately 70% of that produced with typical chrome-moly steels. Because the EDM white layer must be removed, the subsequent stoning or grinding of PX5 is much easier than with other steels. There is also a significant reduction in the incidence of problems involving the hardened layer, such as surface layer cracking or peeling. Consequently, no post EDM stress relieving is needed.
Hardness of EDM Affected Area

  • Polishing
    PX5's exceptional cleanliness, uniform microstructure, and uniform through hardness facilitate excellent and consistent surface finishing characteristics. PX5 polishes faster and easier to a superior mirror finish than common P20-type steels. PX5 will polish to a 6000-7000 grit finish, while P20 polishes to only a 5000 grit finish.

Mirror Surface


  • Photo Etchability
    PX5 is an excellent steel for photo etching. Low chemical segregation of the alloying elements results in a clean, homogenous steel. Absolutely no etch unevenness will occur due to chemical segregation. PX5's uniform hardness and refined grain structure also provide a consistent surface condition for texturing. A reduction in work time and cost can be anticipated due to the elimination of etch unevenness problems.
  • Ion-Nitriding
    Ion-nitriding increases wear resistance and creates a hard surface ideal for slides or molds which will be molding abrasive or mineral-filled thermoplastics. PX5 can be ion-nitrided to produce a surface hardness over 60 HRc without distortion or dimensional changes. This ion-nitrided surface also improves part release and corrosion resistance.
  • Welding
    It is essential that no rod other than PX5 should be used in all welding situations. All other rods are incompatible with the base metal chemistry of PX5 and will produce unacceptable results.

    In most cases, PX5 can be welded with no pre- or post-heating procedures. However, this is not true in all situations. We suggest that in the event a polished surface must be welded (such as a lens or chrome-plated parts), pre-heat the block to between 650-900F. Weld with PX5 rod, then post-heat to between 1040-1050F. Final draw temperature for PX5 mold steel is 1117F.

    DO NOT, under any circumstances, exceed final draw temperature.

    On a textured surface, the need to pre- and post-heat is determined by the etching method used by the grain source. If the selected grainer uses the immersion process with a nitric acid-based solution, then there is generally no need for pre- or post-heating procedures. If the grainer uses a ferric chloride flow technique, it is recommended that a full pre- and post-heating procedure be performed prior to texturing as outlined above.

    We recognize that many mold welders apply heat locally with torches as a means of pre-heating the welded area. While this is a commonly used procedure, and generally produces acceptable results on non-polished surfaces, it is not recommended for post-heating welded blocks. The result of localized heat of this type is an actual flame-hardening of the weld that will produce an inconsistent increase in hardness by as much as 10-12 points (Rockwell C).

    1) Weld Cracking Sensitivity
    The compositional balance of PX5 was designed to suppress crack sensitivity. The weld will not shrink and crack at the marriage line, even without pre- and post-heating, as long as basic welding conditions are observed.

    Y-Split Cracking Test
    (determines cracking susceptibility)
Welding method MAG
Filler rod PX5 Weld Rod
Filler rod Diameter 0.047"
Welding Current 280 A
Gas flow rate 25 /min
Pre/post heating None




Results


PX5

P20

PX5 exhibits no cracking in either the weld surface or interior.

Weld cracking will not occur as long as basic welding conditions and procedures are observed.

2) Weld Hardness
PX5 has the lowest level of hardness in the heat-affected zone of any P20-type mold steel. This relatively low increase in hardness reduces post-weld cutting and grinding times (i.e., high-speed steel end mills can be used).

Hardness Distribution Around Weld


3) Photo Etchability
After weld repair, typical P20 will have etch unevenness due to its increased hardness. This requires many hours to correct. PX5's relatively small increase in hardness in the heat affected zone reduces the incidence of etch unevenness and requires minimal correction work.

Photo Etch Quality Around Weld



4) Distortion
Post-weld distortion is the lowest for any P20-type material, due to the relatively small increase in hardness in the weld area. Post-repair dimensional correction work is simplified.

Test Conditions

Welding method TIG
Filler rod PX5 Weld Rod
Filler rod diameter 0.094"
Welding current 125 A
Gas flow rate 7 /min
Pre/post heating None

Test Method

Results

5) Undercut Characteristics
While undercutting or "sink" surrounding the weld will always occur to some degree, PX5 has only a small degree of undercutting, dramatically reducing the amount of repair time.

Weld Sink

Test Conditions
TIG: 160A, no filler
Test piece: 10 degree slant

Weld Sink at Heat Affected Zone

PX5

P20

4140


All technical and engineering data and suggested procedures, specifications and applications contained in this publication are for general information only. Daido Steel, International Mold Steel and/or their distributors disclaim any and all express or implied warranties of merchantability, suitability for any particular purpose or use, or freedom from infringement of any patent, trademark or copyright. PX5 is a registered trademark of International Mold Steel, Inc. and Daido Steel Limited.

 

PX5

Products

Unique Characteristics

Savings Calculator

Benefits

Mechanical Properties

Physical Properties

General Design Guidelines

Processing Guidelines

Technical Center

 

 
 
  International Mold Steel, Inc. 
6796 Powerline Drive 
Florence, KY 41042 USA 
Toll Free: 800.625.6653
Tel: 859.342.6000
Fax: 859.342.6006
Sales E-mail: salesdesk@imsteel.com
Literature E-mail: info@imsteel.com
Web: www.imsteel.com


www.imsteel.com